![90°C Crosslinkable LSZH Cable Compound]()
90°C Crosslinkable LSZH Cable CompoundModel: EPC9901view more
Product Type: 90°C Irradiation Cross-Linked LSZH Compound
Cross-Linking Method: Electron Beam / Irradiation Cross-Linking
Recommended Irradiation Dose: 10–12... -
![105°C Crosslinkable LSZH Cable Compound]()
105°C Crosslinkable LSZH Cable CompoundModel: EPC9051view more
Product Type: 105°C Crosslinkable LSZH Compound
Cross-Linking Method: Electron Beam / Irradiation Cross-Linking
Recommended Irradiation Dose: 10–12 MRad... -
![105°C High Flame-Retardant LSZH Cable Compound]()
105°C High Flame-Retardant LSZH Cable CompoundItem: EPC9054view more
Product Type: 105°C irradiation cross-linked high flame-retardant LSZH cable compound
Primary Position: High flame-retardant 105°C cable material
Application... -
![125°C Crosslinkable LSZH Cable Compound]()
125°C Crosslinkable LSZH Cable CompoundModel: EPC9251view more
Product Type: 125°C Crosslinkable LSZH Cable Compound
Cross-Linking Method: Electron Beam / Irradiation Cross-Linking
Recommended Irradiation Dose: 10–12... -
![150°C Crosslinkable LSZH Cable Compound]()
150°C Crosslinkable LSZH Cable CompoundModel: EPC9501view more
Product Type: 150°C Crosslinkable LSZH Cable Compound
Cross-Linking Method: Electron Beam / Irradiation Cross-Linking
Recommended Irradiation Dose: 10–12... -
![105°C UL VW-1 XLPO Wire Compound]()
105°C UL VW-1 XLPO Wire CompoundTemperature Rating: 105°Cview more
Tensile Strength: 11.3 MPa
Elongation at Break: 215%
Tensile Strength after Heat Aging: 12.2 MPa
Elongation after Heat Aging: 190% -
![125°C UL FT-2 XLPO Wire Compound]()
125°C UL FT-2 XLPO Wire CompoundDensity: 1.38 g/cm³view more
Melt Index: 11 g/10 min
Tensile Strength: 15.1 MPa
Elongation at Break: 345%
Heat Aging: 158°C × 168 h -
![125°C UL VW-1 Low-Halogen XLPO Compound]()
125°C UL VW-1 Low-Halogen XLPO CompoundHeat Aging: 158°C × 168 hview more
Tensile after Aging: 18.5 MPa
Elongation after Aging: 397%
Oxygen Index: 34%
Hardness: Shore A 95 -
![150°C UL FT-2 XLPO Wire Compound]()
150°C UL FT-2 XLPO Wire CompoundTensile Strength: 15.2 MPaview more
Elongation at Break: 350%
Heat Aging: 180°C × 168 h
Tensile after Aging: 17.9 MPa
Elongation after Aging: 302% -
![150°C UL VW-1 Low-Halogen XLPO Compound]()
150°C UL VW-1 Low-Halogen XLPO CompoundDensity: 1.33 g/cm³view more
Melt Index: 28 g/10 min
Tensile Strength: 16.5 MPa
Elongation at Break: 480%
Heat Aging: 180°C × 168 h
As one of the most professional cross-linked LSZH cable compounds manufacturers and suppliers in China, we also support customized service. We warmly welcome you to buy bulk durable cross-linked LSZH cable compounds from our factory. If you have any enquiry about free sample, please feel free to email us.
150 C low smoke low halogen wire compound, crosslinked polyolefin VW 1 material, VW 1 equipment wire insulation material